| 熔體流動速率 (2.16kg at 220C) | 8.5 | g/10min | ASTM D-1238 |
| 泊松比 | 0.45 | ASTM E-132 | |
| 彎曲模量 | ASTM D-790 IB | ||
| (-40C(-40F)) | 172(25) | MPa(kpsi) | |
| (100C(212F)) | 28(4.1) | MPa(kpsi) | |
| 硬度 | 40 | ASTM D-2240 | |
| IZOD沖擊強度 (23C(73F),6.35mm(0.25in)) | NB | J/m(ft lb/in) | ASTM D-256-A |
| 撕裂強度 | 95(550) | KN/m(lb/in) | ASTM D-1004 |
| 斷裂伸長率 | 700 | % | ASTM D-638 |
| 拉伸應力 (張力 10%) | 3.5(0.5) | MPa(kpsi) | ASTM D-638 |
| IZOD沖擊強度 (-40C(-40F),6.35mm(0.25in)) | NB | J/m(ft lb/in) | ASTM D-256-A |
| 拉伸應力 (張力 5%) | 2.4(0.4) | MPa(kpsi) | ASTM D-638 |
| 斷裂抗拉強度 | 20(2.9) | MPa(kpsi) | ASTM D-638 |
| 彎曲模量 (23C(73F)) | 55(8.0) | MPa(kpsi) | ASTM D-790 IB |
| 熱變形溫度 (0.45MPa(66psi)) | 55(131) | ℃(°F) | ASTM D-648 |
| 維卡軟化點 | 134(273) | ℃(°F) | ASTM D-1525-B |
| 熔點 | 193(379) | ℃(°F) | ASTM D-3418 |
| 厚度等級 | HB | UL 94 | |
| 厚度測試 | 1.56 | mm | UL 94 |
| 比重 | 1.11 | ASTM D-792 |