密度 | 1.07 | g/cm | ASTM D792 |
熔體流動速率 (220℃,10kg) | 7 | g/10min | ASTM D1238 |
模具收縮率 | 0.4-0.7 | % | ASTM D955 |
吸水率 | - | % | ASTM D570 |
拉伸強度 | 460 | kg/cm2 | ASTM D638 |
伸長率 | 30 | % | ASTM D638 |
彎曲強度 | 630 | kg/cm | ASTM D790 |
彎曲模量 | 22000 | kg/cm | ASTM D790 |
IZOD沖擊強度 (3.2mm, 23℃) | 16 | kgcm/cm | ASTM D256 |
洛氏硬度 | 108 | R scale | ASTM D785 |
熱變形溫度 (18.6kgf/cm) | 92(197.6) | ℃(℉) | ASTM D648 |
維卡軟化溫度 (5kg, 50℃/h) | 105(221) | ℃(℉) | ASTM D1525 |
阻燃性 (1.6mm) | HB | UL 94 |