ABS 臺灣奇美 PA-763 耐高溫 阻燃級 注塑級 高流動 汽車部件
物理性能額定值單位測試方法
| 流動系數 (200℃, 5kg) | 2.8 | g/10min | ASTM D-1238 |
| 比重 (23℃) | 1.19 |
| ASTM D-792 |
機械性能額定值單位測試方法
| 引張強度 |
|
| ASTM D-638 |
| (1/8",6mm/min) | 395 | kg/cm |
|
| (1/8",6mm/min) | 5600 | lb/in |
|
| 延伸率 (1/8",6mm/min) | 30 | % | ASTM D-638 |
| 彎曲強度 |
|
| ASTM D-790 |
| (1/4",2.8mm/min) | 620 | kg/cm |
|
| (1/4",2.8mm/min) | 8800 | lb/in |
|
| 彎曲彈性率 |
|
| ASTM D-790 |
| (1/4",2.8mm/min) | 25000 | kg/cm |
|
| (1/4",2.8mm/min) | 350000 | lb/in |
|
| IZOD缺口沖擊強度 |
|
| ASTM D-256 |
| (1/4",23℃) | 20 | kg-cm/cm |
|
| (1/4",23℃) | 3.7 | ft-lb/in |
|
| (1/8",23℃) | 24 | kg-cm/cm |
|
| (1/8",23℃) | 4.4 | ft-lb/in |
|
| 硬度 (1/2") | 98 | R Scale | ASTM D-785 |
熱性能額定值單位測試方法
| 維卡軟化點 |
|
| ASTM D-1525 |
| (1/8",50℃/hr) | 104 | ℃ |
|
| (1/8",50℃/hr) | 104 | ℉ |
|
| 熱變形溫度 |
|
| ASTM D-648 |
| (85℃.8hr ,1/4",120℃/hr) | 96(85) | ℃ |
|
| (85℃.8hr ,1/4",120℃/hr) | 205(185) | ℉ |
|
| 燃燒率 |
|
| UL 94 |
| (1.6mm) | V-0 |
|
|
| (2.5mm) | 5VB |
|
|