| 密度 | 1.43 g/cc | 0.0517 lb/in3 | Crystalline; ISO 1183 |
| Water Absorption at Saturation | 0.40 % @Temperature 23.0 °C | 0.40 % @Temperature 73.4 °F | E; by immersion; ISO 62-1 |
| 0.45 % @Temperature 100 °C | 0.45 % @Temperature 212 °F | immersion; ISO 62-1 | |
| 粘度 | 475000 cP @Temperature 400 °C | 475000 cP @Temperature 752 °F | melt; ISO 11443 |
| 線性成型收縮率,Flow | 0.0030 cm/cm | 0.0030 in/in | 360°C nozzle, 160°C tool; ISO 294-4 |
| 線性成型收縮率，橫向 | 0.0090 cm/cm | 0.0090 in/in | 380°C nozzle, 190°C tool; ISO 294-4 |
| Spiral Flow | 10.0 cm @Thickness 1.00 mm | 3.94 in @Thickness 0.0394 in | 380°C nozzle, 190°C tool |
| 抗張強度(斷裂) | 160 MPa @Temperature 23.0 °C | 23200 psi @Temperature 73.4 °F | ISO 527 |
| 伸長率 (斷裂) | 3.4 % @Temperature 23.0 °C | 3.4 % @Temperature 73.4 °F | ISO 527 |
| 拉伸模量 | 8.80 GPa @Temperature 23.0 °C | 1280 ksi @Temperature 73.4 °F | ISO 527 |
| 彎曲強度 | 250 MPa @Temperature 23.0 °C | 36300 psi @Temperature 73.4 °F | ISO 178 |
| 彎曲模量 | 8.30 GPa @Temperature 23.0 °C | 1200 ksi @Temperature 73.4 °F | ISO 178 |
| 懸壁梁缺口沖擊強度 | 10.0 kJ/m2 @Temperature 23.0 °C | 4.76 ft-lb/in2 @Temperature 73.4 °F | ISO 180/A |
| 懸壁梁無缺口沖擊強度 | 65.0 kJ/m2 @Temperature 23.0 °C | 30.9 ft-lb/in2 @Temperature 73.4 °F | ISO 180/U |
| 體積電阻率 | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| 介電常數 | 3.1 @Frequency 1000 Hz, Temperature 23.0 °C | 3.1 @Frequency 1000 Hz, Temperature 73.4 °F | IEC 60250 |
| 介電強度 | 24.0 kV/mm @Thickness 2.00 mm | 610 kV/in @Thickness 0.0787 in | IEC 60243-1 |
| 耗散因數 | 0.0050 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.0050 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | IEC 60250 |
| 相比耐漏電起痕指數(CTI) | 150 V | 150 V | IEC 60112 |
| 線性熱膨脹系數 | 45.0 μm/m-°C @Temperature <=143 °C | 25.0 μin/in-°F @Temperature <=289 °F | Average below Tg; ISO 11359 |
| 120 μm/m-°C @Temperature >=143 °C | 66.7 μin/in-°F @Temperature >=289 °F | Average above Tg; ISO 11359 | |
| 線形熱膨脹系數 - 流動 | 20.0 μm/m-°C @Temperature <=143 °C | 11.1 μin/in-°F @Temperature <=289 °F | Below Tg; ISO 11359 |
| 22.0 μm/m-°C @Temperature >=143 °C | 12.2 μin/in-°F @Temperature >=289 °F | Above Tg; ISO 11359 | |
| 導熱系數 | 0.350 W/m-K | 2.43 BTU-in/hr-ft2-°F | Along flow; ISO 22007-4 |
| 0.300 W/m-K @Temperature 23.0 °C | 2.08 BTU-in/hr-ft2-°F @Temperature 73.4 °F | Average; ISO/CD 22007-4 | |
| 熔融溫度 | 343 °C | 649 °F | ISO 11357 |
| 載荷下熱變形溫度(1.8 MPa) | 315 °C | 599 °F | ISO 75-f |
| 玻璃化轉變溫度，Tg | 143 °C | 289 °F | Onset; ISO 11357 |
| 150 °C | 302 °F | Midpoint; ISO 11357 |
| 加工溫度 | <= 100 °C | <= 212 °F | Hopper Temperature |
| 射嘴溫度 | 380 °C | 716 °F | |
| 模具溫度 | 170 - 200 °C | 338 - 392 °F | |
| 干燥溫度 | 120 °C @Time 18000 sec | 248 °F @Time 5.00 hour | |
| 150 °C @Time 10800 sec | 302 °F @Time 3.00 hour |
上海韜盛塑化科技有限公司 對比點擊按鈕將公司加入對比列表，詳細對比不同公司差異上海韜盛塑化科技有限公司是一家集貿易與生產研發為一體的商貿公司，代理經營各國各種型號塑膠原料，以及生產各種改性工程塑膠.本公司主更多上海韜盛塑化科技有限公司是一家集貿易與生產研發為一體的商貿公司，代理經營各國各種型號塑膠原料，以及生產各種改性工程塑膠.本公司主要研發生產:ABS、POM、PC、HIPSPMMA、PC/ABS、PA66、PPO、PBT、K膠.....特種工程料：PPS、LCP、PEI、TPX、PA9T、PA6T、PA12、PA46、PTFE、PCTG、TPEE、PEEK、PC/PBT...增強系列：PP、PPS、PPO、PBT、PA、ABS、POM工程系列：PPS、LCP、PTFE、PEI、PPO、PBT、PEEK、PA6T、9T、PA46通用系列：ABS、PC、POM、PMMA、PA66、EVA、PC/ABS、HIPS、GPPS、PP、PVC以上僅為我公司部分供貨目錄。如有需要，歡迎來電來函洽談。