德國蒂森日本神鋼E7024焊條用途德國蒂森低碳鋼電焊條(SMAW Electrodes for Unalloyed Steels)
產品牌號 分類標準及標號 基本化學成份典型值（%） 熱處理 σ0.2 Σ b δ5 AKW
AWS A… EN… C MN Si S≤ P≤ Cr Mo Ni Cu MPA MPA % ℃ J
Phoenix BIAU 5.1: E6013 499: E 42 0 RC 11 0.09 0.50 0.35 0.030 0.030 - - - - AW 420 510 22 +22 50
Phoenix（薄板專用） 5.1: E6012 499: E 42 0 R 12 0.08 0.50 0.35 0.030 0.030 - - - - AW 420 510 22 +20 50
SH Gelb 5.1: E6020 499: E 35 0 A 12 0.09 0.50 0.15 0.030 0.025 - - - - AW 360 460 25 +20 60
Phoenix M 5.1: E6013 499: E 42 0 RR 12 0.09 0.50 0.30 0.030 0.030 - - - - AW 420 510 22 +20 60
Phoenix S 5.1: E6013 499: E 42 0 RR 12 0.09 0.50 0.40 0.030 0.030 - - - - AW 420 510 22 +20 60
Phoenix T 5.1: E6013 499: E 42 0 RR 12 0.08 0.55 0.35 0.030 0.030 - - - - AW 420 510 22 +20 60
SH 5.1: E6013 499: E 42 0 RR 11 0.08 0.55 0.40 0.025 0.020 - - - - AW 420 510 23 +20 55
SH Gelb S 5.1: E6013 499: E 38 0 RA 12 0.09 0.55 0.20 0.030 0.025 - - - - AW 380 460 22 +20 60
SH Gelb B 5.1: E6013 499: E 38 2 RB 12 0.08 0.55 0.20 0.030 0.030 - - - - SR 360 430 24 +20 55
SH Gelb R 5.1: E6013 499: E 38 2 RB 12 0.08 0.55 0.20 0.025 0.025 - - - - AW 380 460 22 +20 75
Union 6013 5.1: E6013 499: E 42 0 RC 11 0.09 0.50 0.35 0.030 0.030 - - - - AW 420 510 22 +20 50
Union 7018 5.1: E7018 499: E 42 5 B 32 H5 0.07 1.20 0.35 0.020 0.020 - - - - SR 400 500 26 -50 47
  E 7018 SSEN LH 5.1: E7018 499: E 42 4 B 32 H5 0.07 1.10 0.50 0.020 0.020 - - - - SR 400 500 24 -40 47
Phoenix D 5.1: E7016 499: E 42 3 B 12 H10 0.06 1.05 0.65 0.020 0.020 - - - - SR 400 520 25 -30 50
SH K 50 W 5.1: E7018-1 499: E 42 5 B 32 H5 0.08 1.20 0.50 0.025 0.025 - - - - SR 360 490 26 -50 47
SH K 52 W 5.1: E7016-1 499: E 42 5 B 12 H5 0.07 1.15 0.40 0.025 0.025 - - - - SR 400 500 26 -50 47
SH K 70 W 5.1: E8018-G 499: E 46 4 B 32 H5 0.07 1.40 0.40 0.020 0.020 - - - - SR 450 520 25 -40 47
Phoenix K 50 R 5.1: E7016 499: E 42 3 B 32 0.06 0.95 0.55 0.025 0.025 - - - - SR 360 490 26 -30 47
Phoenix K 50 5.1: E7015 499: E 42 4 B 42 0.06 1.20 0.50 0.025 0.025 - - - - SR 380 490 27 -40 47
Phoenix 120 K 5.1: E7018-1 499: E 42 5 B 32 H5 0.07 1.20 0.35 0.020 0.020 - - - - SR 400 500 26 -50 47
SH K 70 5.1: E8018-G 499: E 46 4 B 42 H5 0.07 1.60 0.35 0.020 0.020 - - - - SR 450 520 25 -40 47
Phoenix K 90 S 5.1: E7016 499: E 46 4 B 32 H5 0.07 1.35 0.40 0.025 0.025 - - - - SR 450 520 25 +20 130
SH 130 5.1: E7024 499: E 42 0 RR 54 0.07 0.60 0.40 0.025 0.025 - - - - SR 410 470 27 +20 70
Phoenix Rot R 160 5.1: E7024-1 499: E 42 0 RR 53 0.07 0.65 0.35 0.030 0.030 - - - - SR 410 470 26 +20 85
Phoenix Rot R 160 S 5.1: E7024 499: E 42 0 RR 53 0.07 0.60 0.35 0.030 0.025 - - - - SR 410 470 26 +20 70
Phoenix Rot AR 160 5.1: E7024-1 499: E 42 2 RA 53 0.08 0.75 0.28 0.025 0.025 - - - - SR 410 470 27 +20 75
Phoenix Rot BR 160 5.1: E7028 499: E 42 2 RB 53 0.08 0.85 0.30 0.030 0.030 - - - - SR 400 470 27 -20 47
SH 180 5.1: E7024 499: E 42 0 RR 73 0.07 0.70 0.33 0.030 0.025 - - - - AW 440 510 24 ±0 47

11 SAFER CD60 ___
(E8015-B2/B2L) R307 電弧穩定，在引弧特性好，易脫渣，焊縫韌性好，裂紋敏感性小，適于焊接1Cr-0.5Mo鋼的焊接。
12 SAFER CD65
SAFER CD65L __
(E9015-/B3/B3L) R407 電弧穩定，在引弧特性好，且抗高溫（可達650*C氧化乃硫化腐蝕。適于焊接2?Cr-1Mo管道。
13 SAFER CD75 __
(E502-15) R507 電弧穩定，在引弧特性好，且抗高溫（可達650*C氧化乃硫化腐蝕。適于焊接4≈6%Cr-0.5Mo耐熱鋼。
14 SAFER CDV80 ___
(E7Cr-15m) ___ 熔化均勻，在引弧特性好，易脫渣，裂紋敏感性小，適于焊接7≈9%Cr-1Mo耐熱鋼（溫度可達650*C）
15 SAFER CDV95 __
(E505-15m) R707 熔化均勻，在引弧特性好，易脫渣，裂紋敏感性小，適于焊接8≈11%Cr-2Mo耐熱鋼（溫度可達650*）。
16 SAFER Ni50 __
(E8015-C3) __ 熔合良好，在引弧特性好，飛濺少，易脫渣，韌性好，適于焊接在-20*C下適用的含Ni0.5≈1.0%低溫鋼。
17 SAFER Ni55 ___
(E8015-Clm) W607Ni 熔合良好，在引弧特性好，易脫渣，裂紋敏感性小，適于焊接在-60*C下使用的，含Ni0.5≈2.0%低溫鋼。
18 SAFER Ni55VD ___
(E8016-Clm) W607NiX 采用直流電源，焊條接負極，可向下立焊，易脫渣，裂紋敏感性小，適于焊接在-60*C下適用的Ni2低溫鋼。
19 SAFER Ni65 ___
(E8015-C2) W107Ni 熔化良好，在引弧特性好，易脫渣，裂紋敏感性小，適于焊接Ni3.5低溫鋼。