奧地利伯樂BOHLER FOX CN 22/9 N雙相不銹鋼焊條

B?HLER FOX CN 22/9 N Stick electrode
Classifications high-alloyed
EN ISO 3581-A: AWS A5.4:
E 22 9 3 N L R 3 2 E2209-17
Characteristics and field of use
Core wire alloyed, rutile coated stick electrode for welding ferritic-austenitic duplex steels such as
1.4462, UNS 31803. Used primarily in the fields of offshore engineering and chemical industry.
In addition to increased strength and toughness, the weld metal has an exceptional resistance to
stress corrosion cracking due to the high proportion of ferrite. Good pitting resistance according to
ASTM G48 / method A. The 2.0 and 2.5 mm dimensions when used at the DC negative pole are
particularly suitable for vertical up welding of pipes in the root and in the subsequent passes, which
is necessary, for instance, in oilfield engineering. Good AC weldability. All dimensions suitable for
position welding.
Base materials
same-type duplex steels as well as similar-alloy, ferritic-austenitic materials of increased strength
1.4462 X2CrNiMoN22-5-3, 1.4362 X2CrNiN23-4, 1.4462 X2CrNiMoN22-5-3 with 1.4583 X10CrNi-
MoNb18-12, 1.4462 X2CrNiMoN22-5-3 with P235GH/ P265GH, S255N, P295GH, S355N, 16Mo3
UNS S31803, S32205
Typical analysis of all-weld metal (Wt-%)
C Si Mn Cr Ni Mo N PREN
<=0.03 0.8 0.9 22.6 9.0 3.1 0.17 >=35
Mechanical properties of all-weld metal
Heat
Treatment
Yield
strength
0.2%
Tensile
strength
Elongation
(L0=5d0)
Impact values
in J CVN
MPa MPa % +20°C: -10°C: -20°C:
untreated 650 820 25 55 50 ≥ 32
Operating data
Polarity = ± / ~
Dimensions (mm) Amperage A
2.5 x 350 40-75
3.2 x 350 70-120
4.0 x 350 110-160
5.0 x 450 150-200
Approvals and certificates
T?V (3636.), ABS (E 22 09-17), DNV (Duplex), GL (4462), LR (X), RINA (2209), Statoil, SEPROZ,
CE
Similar alloy filler metals
Stick electrode: FOX CN 22/9 N-B Solid wire electrode: CN 22/9 N-IG
TIG rod: CN 22/9 N-IG Flux cored wire: CN 22/9 N-FD
CN 22/9 PW-FD
Wire/flux combination: CN 22/9 N-UP/BB 202